Oxidation of a Dispersion-Strengthened Powder Metallurgical FeCrAl Alloy in the Presence of O2 at 1,100°C: The Influence of Water Vapour
Artikel i vetenskaplig tidskrift, 2015

The oxidation behaviour of the FeCrAl alloy Kanthal(A (R)) APMT in O-2 + N-2 and O-2 + N-2 + H2O environments at 1,100 A degrees C was investigated using thermogravimetry and detailed analyses of the scale morphology with SEM/EDX and STEM/EDX. Wrought FeCrAl alloy Kanthal(A (R)) AF was used as a reference. Exposure time was up to 168 h. Water vapour influenced the early oxide growth kinetics. This effect is explained in terms of water acting as an oxidant, simultaneously with O-2. During later stages of the exposures, H2O had no effect on the kinetics of oxidation.

FeCrAl

High-temperature oxidation

Water vapour

Författare

Kristina M Hellström

Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Niklas Israelsson

Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Nooshin Mortazavi Seyedeh

Chalmers, Teknisk fysik, Materialens mikrostruktur

Sead Canovic

Chalmers, Teknisk fysik, Materialens mikrostruktur

Mats Halvarsson

Chalmers, Teknisk fysik, Materialens mikrostruktur

Jan-Erik Svensson

Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Lars-Gunnar Johansson

Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Oxidation of Metals

0030-770X (ISSN) 1573-4889 (eISSN)

Vol. 83 533-558

Ämneskategorier

Metallurgi och metalliska material

DOI

10.1007/s11085-015-9534-7