Reliability investigation of a carbon nanotube array thermal interface material
Artikel i vetenskaplig tidskrift, 2019

As feature density increases within microelectronics, so does the dissipated power density, which puts an increased demand on thermal management. Thermal interface materials (TIMs) are used at the interface between contacting surfaces to reduce the thermal resistance, and is a critical component within many electronics systems. Arrays of carbon nanotubes (CNTs) have gained significant interest for application as TIMs, due to the high thermal conductivity, no internal thermal contact resistances and an excellent conformability. While studies show excellent thermal performance, there has to date been no investigation into the reliability of CNT array TIMs. In this study, CNT array TIMs bonded with polymer to close a Si-Cu interface were subjected to thermal cycling. Thermal interface resistance measurements showed a large degradation of the thermal performance of the interface within the first 100 cycles. More detailed thermal investigation of the interface components showed that the connection between CNTs and catalyst substrate degrades during thermal cycling even in the absence of thermal expansion mismatch, and the nature of this degradation was further analyzed using X-ray photoelectron spectroscopy. This study indicates that the reliability will be an important consideration for further development and commercialization of CNT array TIMs.

Carbon nanotubes

Thermal aging

Thermal interface material

Thermal management

Reliability

Författare

Andreas Nylander

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

Josef Hansson

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

Majid Kabiri Samani

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

C. C. Darmawan

SHT Smart High-Tech

Ana Borta Boyon

Thales Research and Technology

Laurent Divay

Thales Research and Technology

L. Ye

SHT Smart High-Tech

Yifeng Fu

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

A. Ziaei

Thales Research and Technology

Johan Liu

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

Energies

1996-1073 (ISSN)

Vol. 12 11 2080

Kolbaserat höghastighet 3D GaN elektroniksystem

Stiftelsen för Strategisk forskning (SSF), 2014-03-01 -- 2019-06-30.

Pilot line production of functionalized CNTs as thermal interface material for heat dissipation in electronics applications (SMARTHERM)

Europeiska kommissionen (Horisont 2020), 2016-01-01 -- 2018-12-31.

Nanoteknikstödd tillverkning av högpresterande sinterstål

Stiftelsen för Strategisk forskning (SSF), 2016-01-01 -- 2020-12-31.

Förbättrade cementbaserad ytskydd/reparation materialer med utnyttjande av två-dimensionella material

Formas, 2018-01-01 -- 2020-12-31.

Styrkeområden

Produktion

Ämneskategorier

Energiteknik

Textil-, gummi- och polymermaterial

Kompositmaterial och -teknik

DOI

10.3390/en12112080

Mer information

Senast uppdaterat

2019-07-15