Effect of atomization on surface oxide composition in 316L stainless steel powders for additive manufacturing
Artikel i vetenskaplig tidskrift, 2020

The initial oxide state of powder is essential to the robust additive manufacturing of metal components using powder bed fusion processes. However, the variation of the powder surface oxide composition as a function of the atomizing medium is not clear. This work summarizes a detailed surface characterization of three 316L powders, produced using water atomization (WA), vacuum melting inert gas atomization (VIGA), and nitrogen atomization (GA). X‐ray photoelectron spectroscopy (XPS) and scanning electron microscopy analyses were combined to characterize the surface state of the powders. The results showed that the surface oxides consisted of a thin (~4 nm) iron oxide (Fe2O3) layer with particulate oxide phases rich in Cr, Mn, and Si, with a varying composition. XPS analysis combined with depth‐profiling showed that the VIGA powder had the lowest surface coverage of particulate compounds, followed by the GA powder, whereas the WA powder had the largest fraction of particulate surface oxides. The composition of the oxides was evaluated based on the XPS analysis of the oxide standards. Effects of Ar sputtering on the peak positions of the oxide standards were evaluated with the aim of providing an accurate analysis of the oxide characteristics at different etch depths.

316L

surface oxides

XPS analysis

depth profiling

atomization

additive manufacturing

Författare

Dmitri Riabov

Höganäs

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Eduard Hryha

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Masoud Rashidi

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Nanyang Technological University

Sven Bengtsson

Höganäs

Lars Nyborg

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Surface and Interface Analysis

0142-2421 (ISSN) 1096-9918 (eISSN)

Vol. 52 11 694-706

Ämneskategorier

Bearbetnings-, yt- och fogningsteknik

Korrosionsteknik

Infrastruktur

Chalmers materialanalyslaboratorium

Styrkeområden

Materialvetenskap

DOI

10.1002/sia.6846

Mer information

Senast uppdaterat

2021-05-11