Templated Growth of Covalently Bonded Three-Dimensional Carbon Nanotube Networks Originated from Graphene
Artikel i vetenskaplig tidskrift, 2012
A template-assisted method that enables the growth of covalently bonded three-dimensional carbon nanotubes (CNTs) originating from graphene at a large scale is demonstrated. Atomic force microscopy-based mechanical tests show that the covalently bonded CNT structure can effectively distribute external loading throughout the network to improve the mechanical strength of the material.
covalent bonding
switches
elastic properties
strength
transport
y-junctions
conductivity
mechanism
laser-ablation
membranes
carbon nanotube
arc-discharge method
templated growth
mechanical strength
graphene
Författare
Yifeng Fu
Chalmers, Teknisk fysik, Elektronikmaterial
Björn Carlberg
Chalmers, Teknisk fysik, Elektronikmaterial
Niklas Lindahl
Göteborgs universitet
Niclas Lindvall
Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik
Johan Bielecki
Chalmers, Teknisk fysik, Kondenserade materiens fysik
Aleksandar Matic
Chalmers, Teknisk fysik, Kondenserade materiens fysik
Yuxin Song
Chalmers, Mikroteknologi och nanovetenskap, Fotonik
Zhili Hu
Chalmers, Teknisk fysik, Elektronikmaterial
Zonghe Lai
Chalmers, Mikroteknologi och nanovetenskap, Nanotekniklaboratoriet
L. Ye
SHT Smart High-Tech
Jie Sun
Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik
Y. H. Zhang
Shanghai University
Y. Zhang
Shanghai University
Johan Liu
Chalmers, Teknisk fysik, Elektronikmaterial
Advanced Materials
09359648 (ISSN) 15214095 (eISSN)
Vol. 24 12 1576-1581Styrkeområden
Nanovetenskap och nanoteknik
Materialvetenskap
Ämneskategorier
Fysik
Infrastruktur
Nanotekniklaboratoriet
DOI
10.1002/adma.201104408